| 物理性能 | Rated value | Unit system | Test method |
| 密度 | 1.25 | g/cm³ | ASTM D792 |
| 成型收缩率-流动 | 0.10 to 0.20 | % | ASTM D955 |
| 机械性能 | Rated value | Unit system | Test method |
| 抗张强度3 (屈服, 0.125 in (3.18 mm)) | 12000 psi | MPa | ASTM D638 |
| 弯曲模量 4 (0.125 in (3.18 mm)) | 6890 | MPa | ASTM D790 |
| 弯曲强度 4 (0.125 in (3.18 mm))15000 psi | 103 | MPa | ASTM D790 |
| 冲击性能 | Rated value | Unit system | Test method |
| 悬壁梁缺口冲击强度 | J/m | °C | ASTM D256 |
| 73°F (23°C), 0.125 in (3.18 mm)1.0 ft·lb/in | 53 | J/m | ASTM D256 |
| 热性能 | Rated value | Unit system | Test method |
| 载荷下热变形温度 | ASTM D648 | ||
| 264psi (1.8 MPa)，未退火，0.250 in (6.35毫米) | 102 | °C | ASTM D648 |
| 注射 | Rated value | Unit system | Test method |
| 螺杆转速 | 30 to 60 | rpm | |
| 干燥温度 | 87.8 | 。C | |
| 干燥时间 | 2 | hrs | |
| 干燥时间，最大 40 | . 4.0 | ||
| 加工（熔体）温度 | 232 to 260 | °C | |
| 模具温度 | 48.9 to 65.6 | 。C | |
| 背压 | 0.689 to 2.07 | MPa |